供應(yīng)ABS/臺灣奇美/PA-757

性能項目測試條件測試方法數(shù)值/描述單位機(jī)械性能拉伸強(qiáng)度(引張強(qiáng)度) ASTM D638/ISO 527490(6,950)kg/cm2(MPa)[Lb/in2]斷裂伸長率 ASTM D638/ISO 527-%拉伸模量 ASTM D638/ISO 527-kg/cm2(MPa)[Lb/in2]拉伸屈服伸長率(延伸率) ASTM D638/ISO 52720%拉伸斷裂伸長率(延伸率) ASTM D638/ISO 527-%彎曲模量(彎曲彈性率) ASTM D790/ISO 17827000(38000)kg/cm2(MPa)[Lb/in2]彎曲強(qiáng)度 ASTM D790/ISO 178790(11,660)kg/cm2(MPa)[Lb/in2]洛氏硬度 ASTM D785R-116 IZOD 缺口沖擊強(qiáng)度1/4" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 17917(3.1)kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 17920(3.7)kg·cm/cm(J/M)ft·lb/inCharpy沖擊強(qiáng)度23℃ （缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in23℃（無缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（無缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.05 成型收縮率 ASTM D955-%熔融指數(shù)（流動系數(shù)）200℃/5kgASTM D1238/ISO 11331.6g/10min220℃/10kgASTM D1238/ISO 113322g/10min吸水率 23℃/24H ASTM D570/ISO 62-%熱性能熱變形溫度退火ASTM D648/ISO 7599(210)℃（℉）未退火ASTM D648/ISO 7588(190)℃（℉）維卡軟化點 ASTM D1525/ISO R306105(221)℃（℉）熔點 --℃（℉）燃燒性（率） UL941.6mmHB 線性膨脹系數(shù) ASTM D696/ISO 11359-mm/mm.℃加工條件干燥條件 80°C下烘料約2~3小時 加工溫度射嘴 180~230°C℃料筒前段 190~230℃料筒中段 190~230℃料筒后段 180~220℃熔體溫度 -℃模具溫度 30~70°C℃壓力注塑壓力 -Mpa保壓壓力 -Mpa背壓 -Mpa螺桿轉(zhuǎn)速 -rpm其他備注-顏色-特性高光澤性 高剛性。用途電視機(jī)前殼 / 復(fù)印機(jī)外殼 / 電話機(jī)殼 / 化妝品盒 / 輪胎蓋